Hlavní stránka>BS EN 61249-2-9:2003 Materials for interconnection structures. Sectional specification set for reinforced base materials, clad and unclad Reinforced base materials clad and unclad. Bismaleimide/triazine, modified epoxide or unmodified, woven E-glass reinforced laminated sheets of defined flammability (vertical burning test), copper-clad
sklademVydáno: 2003-08-14
BS EN 61249-2-9:2003 Materials for interconnection structures. Sectional specification set for reinforced base materials, clad and unclad Reinforced base materials clad and unclad. Bismaleimide/triazine, modified epoxide or unmodified, woven E-glass reinforced laminated sheets of defined flammability (vertical burning test), copper-clad

BS EN 61249-2-9:2003

Materials for interconnection structures. Sectional specification set for reinforced base materials, clad and unclad Reinforced base materials clad and unclad. Bismaleimide/triazine, modified epoxide or unmodified, woven E-glass reinforced laminated sheets of defined flammability (vertical burning test), copper-clad

Formát
Dostupnost
Cena a měna
Anglicky Zabezpečené PDF
K okamžitému stažení
6240 Kč
Čtěte normu po dobu 1 hodiny. Více informací v kategorii E-READING
Čtení normy
na 1 hodinu
624.00 Kč
Čtěte normu po dobu 24 hodin. Více informací v kategorii E-READING
Čtení normy
na 24 hodin
1872.00 Kč
Anglicky Tisk
Skladem
6240 Kč
Označení normy:BS EN 61249-2-9:2003
Počet stran:26
Vydáno:2003-08-14
ISBN:0 580 42390 5
Status:Standard
Popis

BS EN 61249-2-9:2003


This standard BS EN 61249-2-9:2003 Materials for interconnection structures. Sectional specification set for reinforced base materials, clad and unclad is classified in these ICS categories:
  • 31.180 Printed circuits and boards
Gives requirements for properties of bismaleimide/triazine modified epoxide, or unmodified, woven E-glass reinforced laminate sheets of defined flammability, copper-clad in thicknesses of 0,05 mm to 3,2 mm. The flammability rating is achieved through the use of fire retardants contained as an integral part of the epoxide polymeric structure.