Vážení zákazníci, v letošním roce budeme expedovat poslední objednávky ve středu 18. 12. 2024.

Těšíme se s vámi na shledanou od pondělí 06. 01. 2025.

 

Přihlásit seRegistrovat se
Jazyk czen
Menu
KontaktOBCHODNÁPOVĚDAInfobarE-ReadingNovinky
Hledání
0
Celková cena
0 Kč
Cena s DPH / bez DPH
Hlavní stránka>BS EN ISO 23146:2016 Fine ceramics (advanced ceramics, advanced technical ceramics). Test methods for fracture toughness of monolithic ceramics. Single-edge V-notch beam (SEVNB) method
Sponsored link
sklademVydáno: 2016-05-31
BS EN ISO 23146:2016 Fine ceramics (advanced ceramics, advanced technical ceramics). Test methods for fracture toughness of monolithic ceramics. Single-edge V-notch beam (SEVNB) method

BS EN ISO 23146:2016

Fine ceramics (advanced ceramics, advanced technical ceramics). Test methods for fracture toughness of monolithic ceramics. Single-edge V-notch beam (SEVNB) method

Formát
Dostupnost
Cena a měna
Anglicky Zabezpečené PDF
K okamžitému stažení
6820 Kč
Čtěte normu po dobu 1 hodiny. Více informací v kategorii E-READING
Čtení normy
na 1 hodinu
682.00 Kč
Čtěte normu po dobu 24 hodin. Více informací v kategorii E-READING
Čtení normy
na 24 hodin
2046.00 Kč
Anglicky Tisk
Skladem
6820 Kč
Označení normy:BS EN ISO 23146:2016
Počet stran:26
Vydáno:2016-05-31
ISBN:978 0 580 91173 6
Status:Standard
Popis

BS EN ISO 23146:2016


This standard BS EN ISO 23146:2016 Fine ceramics (advanced ceramics, advanced technical ceramics). Test methods for fracture toughness of monolithic ceramics. Single-edge V-notch beam (SEVNB) method is classified in these ICS categories:
  • 81.060.30 Advanced ceramics

This International Standard specifies a method for the determination of the fracture toughness of advanced technical ceramics. The procedure makes use of single-edge V-notched bars, which are loaded in four-point bending until failure. It is applicable to monolithic ceramics with a grain size or major microstructural feature size larger than about 1 µm.

The use of this International Standard for yttria tetragonal zirconia polycrystal material (Y-TZP) is not recommended. The method might also be unsuitable for some other very tough or soft ceramics in which a sharp crack does not form at the root of the V-notch.