Homepage>BS 7034-4:1988 Viscosity and viscometric fixed points of glass Method for the determination of viscosity by beam bending
sklademVydáno: 1989-01-31
BS 7034-4:1988 Viscosity and viscometric fixed points of glass Method for the determination of viscosity by beam bending

BS 7034-4:1988

Viscosity and viscometric fixed points of glass Method for the determination of viscosity by beam bending

Format
Availability
Price and currency
Anglicky Secure PDF
Immediate download
178.32 €
You can read the standard for 1 hour. More information in the category: E-reading
Reading the standard
for 1 hour
17.83 €
You can read the standard for 24 hours. More information in the category: E-reading
Reading the standard
for 24 hours
53.50 €
Anglicky Hardcopy
In stock
178.32 €
Označení normy:BS 7034-4:1988
Počet stran:20
Vydáno:1989-01-31
ISBN:0 580 16903 0
Status:Standard
DESCRIPTION

BS 7034-4:1988


This standard BS 7034-4:1988 Viscosity and viscometric fixed points of glass is classified in these ICS categories:
  • 81.040.01 Glass in general

This part of ISO 7884 specifies a method of determining the dynamic viscosity of glass on a rod-shaped test specimen (called a beam) supported at its ends. The viscous deflection rate of the beam is measured under a given load at the midpoint between the supports. In addition the viscosity-temperature relationship and the dependence of the viscosity on the thermal history of the sample can be determined.

The viscosity range covered by this method extends from 109 to 1015 dPa s2), corresponding to measuring temperatures between about 900 and 400 °C for all glasses of normal bulk-production compositions.

The procedures are limited to small deflections and to small deflection rates (see 3.6).

NOTE During beam bending, elongation flows of both signs occur (zero passage within the neutral plane). The determination of shear viscosity is possible only with Newtonian or linear-viscoelastic behaviour of the glass. The procedures are sensitive to interference by devitrification of the sample. With viscosities above 1012 dPa s the adjustment of the structure equilibrium within the glass is perceptibly delayed with respect to the temperature setting. For tests within this range it should be agreed whether it is necessary to wait for the final equilibrium viscosity at a given temperature or to take the viscosity value corresponding to a conventional temperature-time programme (see 6.3).