Homepage>BS EN 61788-18:2013 Superconductivity Mechanical properties measurement. Room temperature tensile test of Ag- and/or Ag alloy-sheathed Bi-2223 and Bi-2212 composite superconductors
Sponsored link
sklademVydáno: 2014-01-31
BS EN 61788-18:2013 Superconductivity Mechanical properties measurement. Room temperature tensile test of Ag- and/or Ag alloy-sheathed Bi-2223 and Bi-2212 composite superconductors

BS EN 61788-18:2013

Superconductivity Mechanical properties measurement. Room temperature tensile test of Ag- and/or Ag alloy-sheathed Bi-2223 and Bi-2212 composite superconductors

Format
Availability
Price and currency
Anglicky Secure PDF
Immediate download
318.39 €
You can read the standard for 1 hour. More information in the category: E-reading
Reading the standard
for 1 hour
31.84 €
You can read the standard for 24 hours. More information in the category: E-reading
Reading the standard
for 24 hours
95.52 €
Anglicky Hardcopy
In stock
318.39 €
Označení normy:BS EN 61788-18:2013
Počet stran:42
Vydáno:2014-01-31
ISBN:978 0 580 70783 4
Status:Standard
DESCRIPTION

BS EN 61788-18:2013


This standard BS EN 61788-18:2013 Superconductivity is classified in these ICS categories:
  • 17.220.20 Measurement of electrical and magnetic quantities
  • 29.050 Superconductivity and conducting materials
IEC 61788-18:2013 specifies a test method detailing the tensile test procedures to be carried out on Ag/Bi-2223 and Ag/Bi-2212 superconductive composite wires at room temperature. This test is used to measure the modulus of elasticity and to determine the 0,2 % proof strength. When the 0,2 % proof strength could not be determined due to earlier failure, the stress level at apparent strains of 0,05 %, 0,1 %, 0,15 %, 0,2 %, 0,25 % with increment of 0,05 % is measured. The values for elastic limit, fracture strength, percentage elongation after fracture and the fitted type of 0,2 % proof strength serve only as a reference. The sample covered by this test procedure should have a round or rectangular cross-section with an area of 0,3 mm 2 to 2,0 mm 2 (corresponding to the tape-shaped wires with width of 2,0 mm to 5,0 mm and thickness of 0,16 mm to 0,4 mm). Key words: superconductivity, mechanical properties measurement